Tien piikkien ankkurointivoimaan vaikuttavat tekijät ja menetelmät niiden parantamiseksi
- Mitkä ovat ytimen tekijät, jotka vaikuttavat piikin ankkurointivoimaan?
The strength of anchoring materials is crucial. The compressive strength of sulfur anchoring agent must be ≥40MPa; if it is lower than 30MPa, the anchoring force will decrease by 30% - 40%. The water - cement ratio must be controlled within the range of 0.3 - 0.35. The fit gap between the nail hole diameter and the spike should be moderate. An excessively large gap (>3mm) vähentää ankkurointivoimaa 20% - 25%, kun taas liian pieni aukko (<1mm) makes it difficult for the anchoring agent to fill. The optimal gap is 1.5 - 2mm to ensure uniform wrapping force. Insufficient spike embedding depth (<100mm) will reduce the anchoring force by 40% - 50%. The standard embedding depth should be 120 - 150mm, and the embedded part must have threads or barbs to increase mechanical biting force. Insufficient pouring of anchoring agent (voids >5%) aiheuttaa paikallisen stressipitoisuuden, ja ankkurointivoiman heilahtelu saavuttaa 15%- 20%. Paineen kaatamista on käytettävä kompaktiuden varmistamiseksi .
- Mitkä ovat piikin ankkurointivoiman erot eri ankkurointimateriaalien keskuudessa?
Rikki -ankkurointiaineen (rikki: sementti: hiekka=1: 0 . 3: 1 . 5) ankkurointivoima 60 - 80 kN, nopealla asetuksella (30 minuuttia), mutta se on helppo omaksua alhaisella lämpötilassa (ankkurointivoimat vähenee 20%: lla- 20 -asteessa) Rautateiden . hartsin ankkurointiaineen (epoksihartsin + kovetusaineen) ankkurointivoima 80 - 100 kN, jolla on hyvä säänkestävyys . Ankkurointivoiman muutos on pienempi tai yhtä suuri kuin 10% - 40 - 60 aste, mutta sen kustannukset ovat 50% - 60%: lla. Rautatiellä ja kylmäalueilla . sementtilaastin ankkurointiaineella on alhaisempi ankkurointivoima ({40 - 60 kN), mutta hyvä ympäristönsuojaus, joka sopii kaupunkikisan kuljetukseen . 5% - 8% 膨胀剂 膨胀剂 on lisättävä kompensointiin ja vältetään ankkurointia. 100 - 120 kN: n voima. Kun teräskuitupitoisuus on 3% - 5%, leikkauslujuus kasvaa 25% - 30%, jota käytetään raskasten rautateiden avainosissa.
- Kuinka rakennusprosessi vaikuttaa piikin ankkurointivoimaan?
Incomplete cleaning of nail holes (residual dust >5%) vähentää ankkurointivoimaa 15%- 20%. korkean paineilmapistoolia on käytettävä puhdistukseen, ja vaijeriharjoja on käytettävä tarvittaessa varmistaakseen, että kelluvaa kuonaa kynsireiän sisäseinään ({5}} liian matala kaatamislämpötila ankkurointiaineen (<130℃ for sulfur anchoring) will lead to poor fluidity and incomplete filling, reducing the anchoring force by 25% - 30%. The pouring temperature must be controlled at 140 - 160℃. A deviation of spike insertion depth >5mm tekee ankkurointivoiman jakautumisesta epätasaisen, ja samassa erässä olevien piikkien ankkurointivoimaerot voivat saavuttaa 10% - 15% . Paikannustyökaluja on käytettävä insertion aikana yhdenmukaisen syvyyden varmistamiseksi.<24 hours) will make the anchoring agent strength not up to standard, and the anchoring force is only 70% - 80% of the design value. Resin anchoring agent needs to be cured for more than 48 hours, and sulfur anchoring agent needs to be naturally cooled to room temperature (≥6 hours).
- Kuinka ympäristötekijät vaikuttavat piikkien ankkurointiin?
A humid environment will reduce the bonding force between the anchoring agent and the nail hole. When the relative humidity is >90%, the anchoring force decreases by 10% - 15%. Rainy day construction must take rainproof measures to ensure that the nail hole is dry (moisture content ≤5%). A high - temperature environment (≥35℃) will accelerate the curing of resin anchoring agent, and concentrated reaction heat release may cause internal cracking, with an anchoring force loss of 20% - 25%. Retarders must be added to the anchoring agent to extend the gel time to 30 - 40 minutes. Freeze - thaw cycles (- 20 - 20℃) will cause microcracks in the anchoring agent. After 200 cycles, the anchoring force decreases by 30% - 40%. Frost - resistant anchoring agent (adding air - entraining agent, air content 3% - 5%) must be selected in cold regions. Saline - alkaline soil will erode the anchoring agent. When the chloride ion concentration is >500 mg/l, ankkurointivoima heikentää 5% - 8% vuosittain . anti - korroosiopäällystetyt piikit ja alkali - kestävä ankkurointiaine on käytettävä rannikkoalueilla .}}}}}}}}}}}
- Mitkä ovat erityiset toimenpiteet piikin ankkurointivoiman parantamiseksi?
Ankkurointiaineen kaava optimoi: 5% - 8% grafiittijauheen lisääminen rikkiankkurointiaineeseen voi lisätä ankkurointivoimaa 10% - 15% ja parantaa juoksevuutta; Lisäämällä 1% - 2% silaanikytkentäaine hartsin ankkurointiaineen parantamiseen parantaa rajapinnan sitoutumisvoimaa piikkeillä . omaksua mekaaninen ankkurointiapu: vinojen linjojen rullaaminen (sävelkorkeus 3 - 4 mm) Spike -pinnan lisäämiseksi mekaanisen purkamisvoiman kanssa ankkurointiaineen kanssa, lisäämällä ankkurointivoimaa 20%: lla%: - 25%. Raskas - kuljetusrautatiepiikien on otettava käyttöön tämä rakenne {. parantaa rakennusprosessia: Kynsireiän ({40 - 50 asteen) esikäsittely parantaa ankkurointiaineen sujuvuutta, mikä lisää täyttöä varten {16%}}}}}}}}}%: lla, erityisesti talvi -rakennetta.}}}}}}}}} Ankkurointivoima: 10% tavanomaisten rautateiden piikkeistä otetaan näytteitä joka toinen vuosi . niistä, joiden ankkurointivoima on alle 80% suunnitteluarvosta, on ankkuroida {. korkean nopeuden rautatiet havaitaan kerran vuodessa varmistaakseen, että ankkurointivoima täyttää standardin (suurempi kuin yhtä suuri kuin 60) .}}}}}}}}}}